3319チタン茶マットNo.2 (1.8L) new The synthetic Gosu currently used

The synthetic Gosu currently used throughout Japan was developed by the Fukaumi family during the early Meiji period (late 19th century)

【shipping】

please discard the tap water approximately three days after using the glaze

As a general rule

磁器の場合：天草撰中

3319チタン茶マットNo.2 (1.8L) new The synthetic Gosu currently used[Firing conditions for sample plates] Clay components <br>For porcelain: Amakusa Senchu (SiO2 72. 04% Al2O3 18. 16% Fe2O3 0. 65% TiO2 0. 04% CaO 0. 49% MgO 0. 09% Na2O 0. 58% K2O 3. 00% Ig. Loss 4. 55%) For pottery: Umezaki red clay (SiO2 72. 11%, Al2O3 15. 98%, Fe2O3 2. 12%, TiO2 0. 67%, CaO 0. 12%, MgO 0. 36%, Na2O 0. 58%, K2O 2. 47%, Ig. Loss 5. 16%) Firing temperature : Reduction: 1280 Glazing : Baume concentration 50 (soak for about 3 seconds)