70ライラック釉(1.8L) glazes Firing temperature : Reduction: 1280℃

Firing temperature : Reduction: 1280℃ Oxidation: 1250℃

You will not need to hand-grind the pigment yourself once it arrives

the chemical method of producing the color blue using cobalt

ワグネル氏は深海平左衛門、墨之助、竹治父子にドイツでは青の色を出すのにコバルトを用いている事を伝えます。

blue and white porcelain (Sometsuke) and Somenishiki ware created using Fukaumi Shouten's Gosu (blue underglaze) have been beloved by royalty and aristocrats worldwide

70ライラック釉(1.8L) glazes Firing temperature : Reduction: 1280℃[Firing conditions for sample plates] Clay components <br>For porcelain: Amakusa Senchu (SiO2 72. 04% Al2O3 18. 16% Fe2O3 0. 65% TiO2 0. 04% CaO 0. 49% MgO 0. 09% Na2O 0. 58% K2O 3. 00% Ig. Loss 4. 55%) Firing temperature : Reduction: 1280 Oxidation: 1230 Glazing : Baume concentration 50 (soak for about 3 seconds) [How to use] Soil type: porcelain, pottery Possible firing method: oxidation and reduction possible Appropriate firing temperature: 1230